440C Stainless Steel Strip Thickness 0.4 - 6.0mm Cold Rolled SS
Strip UNS S44004
STAINLESS STEEL 440 STRIP GENERAL PROPERTIES:
Stainless steels 440 Strips are high-alloy steels which have high
corrosion resistance compared to other steels due to the presence
of large amounts of chromium. Based on their crystalline structure,
they are divided into three types such as ferritic, austenitic, and
martensitic steels. Another group of stainless steels are
precipitation-hardened steels. They are a combination of
martensitic and austenitic steels. Grade 440C stainless steel strip
is a high carbon martensitic stainless steel. It has high strength,
moderate corrosion resistance, and good hardness and wear
resistance. Grade 440C strip is capable of attaining, after heat
treatment, the highest strength, hardness and wear resistance of
all the stainless alloys. Its very high carbon content is
responsible for these characteristics, which make 440C particularly
suited to such applications as ball bearings and valve parts.
Our Stainless steel 440 strips capabilities include:
- Stainless steel 440 strips Annealed & Precision
- Stainless steel 440 strips thickness-0.1mm to 6.00mm
- Stainless steel 440 strips width-2.5mm to 1320mm (slit to close
tolerances)
Our Stainless steel 440 Cold rolled mill finish strips such as:
- Stainless steel 440 strips 2D - cold rolled, heat treated, pickled.
- Stainless steel 440 strips 2B - cold rolled, heat treated, pickled,
skin passed on bright rolls.
- Stainless steel 440 strips 2R(BA) - cold rolled, bright annealed
- Stainless steel 440 strips HR - hot rolled, annealed
STAINLESS STEEL 440 STRIP APPLICATIONS:
Typical applications include:
- Rolling element bearings
- Valve seats
- High quality knife blades
- Surgical instruments
- Chisels
STAINLESS STEEL 440 STRIP CORROSION RESISTANCE:
Good resistance to the atmosphere, fresh water, foods, alkalies and
mild acids. Best resistance in the hardened and tempered and
passivated condition. A smooth polished surface also assists.
The corrosion resistance of grade 440C approximates that of grade
304 in many environments.
STAINLESS STEEL 440 STRIP HEAT RESISTANCE:
Not recommended for use in temperatures above the relevant
tempering temperature, because of reduction in mechanical
properties by over-tempering.
STAINLESS STEEL 440 STRIP HEAT TREATMENT:
Annealing – Full anneal – 850-900°C, slow furnace cool to about
600°C and then air cool. Sub-critical Annealing – 735-785°C and
slow furnace cool.
Hardening – Heat to 1010-1065°C, followed by quenching in warm oil
or air. Oil quenching is necessary for heavy sections. Immediately
temper at 150-370°C to obtain a wide variety of hardness values and
mechanical properties as indicated in the accompanying table.
Tempering in the range 425-565°C is to be avoided because of
reduced impact resistance and corrosion resistance. Tempering in
the range 590-675°C results in lower hardness (the product become
machinable) and high impact resistance.
STAINLESS STEEL 440 STRIP WELDING:
If welding is necessary pre-heat at 250°C and follow welding with a
full anneal. Grade 420 filler will give a high hardness weld
(although not as high as the 440C), but 309 or 310 will produce
soft welds with higher ductility.
STAINLESS STEEL 440 STRIP MACHINING:
In the annealed condition this grade is relatively easily machined;
approximately the same as for high speed steel. Chips are tough and
stringy so chip breakers are important. If these grades are
hardened machining becomes more difficult and probably impossible.
STAINLESS STEEL 440 STRIP COMPOSITION:
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N |
|---|
| 440C | min. max. | 0.95 1.20 | - 1.00 | - 1.00 | - 0.040 | - 0.030 | 16.00 18.00 | - 0.75 | - | - |
STAINLESS STEEL 440 STRIP MECHANICAL PROPERTIES:
Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell (HR C) | Impact Charpy V (J) |
|---|
| Annealed* | 758 | 448 | 14 | 269HB max# | - |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 316 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
| * Annealed properties are typical for Condition A of ASTM A276#
Brinell Hardness is ASTM A276 specified maximum for annealed 440A,
B and C. |
STAINLESS STEEL 440 STRIP PHYSICAL PROPERTIES:
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (mm/m/°C) | Thermal Conductivity(W/m.K) | Specific Heat
0-100°C (J/kg.K) | Electrical Resistivity (nW.m) |
|---|
| 0-100°C | 0-200°C | 0-600°C | at 100°C | at 500°C |
| 440 C | 7650 | 200 | 10.1 | 10.3 | 11.7 | 24.2 | - | 460 | 600 |
STAINLESS STEEL 440 STRIP POSSIBLE ALTERNATIVE GRADES:
Grade | Why it might be chosen instead of 440C |
|---|
| 440A/B | Slightly softer and more corrosion resistant grade needed |
| 440F | High machinability required, with same hardness and hardenability
as 440C |
| 420 | Lower strength and hardness needed than any of the 440 grades |
| 416 | Higher machinability required, and the much lower hardness and
strength is still adequate |