4Cr13 Stainless Steel Introduction
4Cr13 steel (New name: 40Cr13) is a martensitic type stainless
steel, which has higher hardness than 3Cr13
steel after quenching. The steel has good mechanical processing
performance. After heat treatment (quenching and tempering), it has
good corrosion resistance, polishing performance, high strength and
wear resistance.
4Cr13 Steel Datasheet and Specification
The following tables list the 4Cr13 steel datasheets such as
chemical composition and mechanical properties, etc.
Chemical Composition
| 4Cr13 Chemical Composition (%) |
| Steel Grade | C | Si (≤) | Mn (≤) | P (≤) | S (≤) | Cr | Ni (≤) |
| 4Cr13 (40Cr13) | 0.36-0.45 | 0.60 | 0.80 | 0.040 | 0.030 | 12.00-14.00 | 0.60 |
Mechanical Properties for Steel Bars
- HRC hardness: ≥ 50 (Quenched and Tempered)
- HBW hardness: ≤ 235 (Annealed)
Notes: For diameter or thickness ≤ 75 mm.
Physical Properties
- Density (g/cm3): 7.75
- Specific heat capacity (J/Kg·K): 460 at 0-100℃
- Thermal conductivity (W/m·K):
- Coefficients of linear thermal expansion (10-6/K):
- 10.5 (0-100℃)
- 12.0 (0-500℃)
- Electrical Resistivity (μΩ·m): 0.59 at 20℃
- Longitudinal modulus of elasticity (kN/mm2): 215 at 20℃
Typical Heat Treatment
- Annealing: 800 – 900 ℃ (Slow cooling)
- Quenching: 1050 – 1100 ℃ (Oil cooling)
- Tempering: 200 – 300 ℃ (Air cooling)
Forging
Oil quenching cold work die steel has some crack sensitivity. It
should not be heated quickly when forging heating. It’s better to
preheat at 650-750 °C. The forging heating temperature is 1130-1150
°C, and the final forging temperature should be greater than
800-850 °C. The upper limit temperature is taken when the ingot is
forged, and the lower limit temperature is taken when the billet is
forged.
Applications
Stainless steel 4Cr13 is suitable for manufacturing plastic molds,
transparent plastic products moulds, etc. which are subjected to
high load, high wear resistance and corrosive medium. Also used in
the manufacture of hot oil pumps, tools, valve seats, valves,
nozzles, measuring tools, medical equipment, springs, etc.
(40Cr13) 4Cr13 Steel Equivalent
40Cr13 (4Cr13 stainless steel) equivalent to US ASTM AISI, European
(Germany DIN, UK BSI, France NF), Japanese JIS, and ISO standard.
| China | European | ISO |
| Standard | Grade | Standard | Grade (Steel number) | Standard | Steel Name (ISO Number) |
GB/T 1220;
GB/T 3280 | 4Cr13 (40Cr13) | EN 10088-3 | X39Cr13 (1.4031) | ISO 15510 | X39Cr13 (4031-420-00-I) |