Nickel Alloy Inconel 600 Plate Thickness 0.5 - 30.0mm Alloy 600 Sheet According to ASTM SB168 B

Alloy 600 is a nonmagnetic, nickel-based high temperature alloy possessing an excellent combination of high strength, hot and cold workability, and resistance to ordinary form of corrosion.
This alloy also displays good heat resistance and freedom from aging or stress corrosion throughout the annealed to heavily cold worked condition range.

Applications of Inconel 600 Niickel Alloy Sheet

Some typical applications are:

• Barge and tank truck liners
• Carburizing atmospheres
• Ethylene dichloride crackers
• Furnace trays, mufflers, hangers
• Gasoline stabilizer production
• MgCl2 evaporates
• Phenol condensers
• Soap manufacture
• Titanium dioxide
• Vegetable and fatty acid vessels

Corrosion Resistance of Inconel 600

The high chromium content of alloy 600 raises its oxidation resistance considerably above that of pure nickel, while its high nickel content provides good corrosion resistance under reducing conditions.
This alloy exhibits high levels of resistance to stress and salt water, exhaust gases, and most organic acids and compounds.

Heat Treatment of Inconel 600

Alloy 600 is not an age hardening alloy; cold working is the only available means of hardening. Softening by annealing begins at about 1600°F (871°C), and is reasonably complete after 10 to 15 minutes of heating at 1800°F (982°C). Above this temperature, grain growth may be objectionable, although very brief heating at 1900°F will cause complete softening without undue grain growth. Since the rate of cooling has no effect on the softening, the material may be water quenched or air cooled.

Workability of Inconel 600

Hot Working/Forging

Low sulfur reducing furnace atmospheres should be used in forging. Major hot working should be done between 2300/1850°F, while light working may be continued as low as 1600°F. No hot working should be attempted between 1600/1200°F due to lower ductility in that range.

Machinability

Alloy 600 is machinable in both the hot worked and annealed conditions. Because considerable heat is generated in machining this alloy, high-speed steel, cast nonferrous or cemented carbide tools should be used. The tools should be kept sharp.
Lathe turning speeds with high-speed and nonferrous tools are 35/45 sfm (0.18/0.23 m/s); speeds with cemented carbide tools are 100/175 sfm (0.51/0.89 m/s). (This data should be used as a guide for initial machine setup only. The figures used are averages. On certain work, the nature of the part may require adjustment of speeds and feeds.)
Sulfur-based oil should be used as a lubricant, but should be completely removed before the machined part is exposed to elevated temperatures, as in welding.

Cold Working

For higher properties, alloy 600 can be cold worked below 1200°F (649°C).

Welding
Alloy 600 can be joined by the usual welding , brazing, and soldering process.

Typical Mechanical Properties of Alloy 600

Typical Mechanical Properties
Various forms and conditions

Average Room Temperature Tensile Data

Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe best-selling consumer market. Without our products among consumers enjoy a higher status, the company with a number of retailers and agents to establish a long-term stable cooperative relationship. Our distribution of stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe variety complete, reasonable price. The strength of the company, heavy credit, abide by the contract, ensure product quality, with a variety of management characteristics and the principle of small profits, to win the trust of our customers.