| Grade | Thickness | Size | Surface | Other Size |
| 304 | 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm | 1000 x 2000mm 1219 x 2438mm | BA 8K HL 2B SB NO.4 with PVC film | 1500mm width |
| 316L | 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm | 1000 x 2000mm 1219 x 2438mm | BA 8K HL 2B SB NO.4 with PVC film | 1500mm width |
| 410S | 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm | 1000 x 2000mm 1219 x 2438mm | BA 8K HL 2B SB NO.4 with PVC film | |
| 430 | 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm | 1000 x 2000mm 1219 x 2438mm | BA 8K HL 2B SB NO.4 with PVC film | |
Stainless steel is an alloy steel whose main component is iron,
while containing at least 11% chromium, as well as other elements
such as nickel, molybdenum, manganese and so on. The following are
some properties of stainless steel:
Stainless steel grade 430 is a non-hardenable steel containing
straight chromium, and belongs to the ferritic group of steels.
This steel is known for its good corrosion resistance and
formability, coupled with practical mechanical properties. It can
be used in certain chemical applications due to its resistance to
nitric acid.
Corrosion resistance: Stainless steel is known for its excellent
corrosion resistance. The chromium element reacts with oxygen to
form a dense oxide film (chromium oxide layer), which prevents
further oxidation and corrosion on the surface of the steel, making
the stainless steel resistant to the erosion of most chemical
media. This makes stainless steel widely used in environments
containing water, gases and chemicals.
High temperature performance: stainless steel maintains good
performance at high temperatures and can maintain structural
stability and strength for a long time. This makes stainless steel
suitable for high-temperature processes and applications, such as
petrochemical, energy production and other fields.
Mechanical properties: Stainless steel has excellent mechanical
properties, including strength, hardness and ductility. This makes
stainless steel widely used in manufacturing industries, including
automotive, aerospace, construction and manufacturing.
Aesthetic: The surface of stainless steel is smooth and uniform,
and it can show different appearance effects by polishing, brushing
or painting. This makes stainless steel in architectural
decoration, furniture manufacturing, art production and other
fields have a wide range of applications.
Renewable: Stainless steel is a recyclable material, through
recycling and reuse, can reduce resource consumption and
environmental pollution, in line with the principle of sustainable
development.
In general, stainless steel has excellent properties such as
corrosion resistance, high temperature resistance, good mechanical
properties, aesthetics and renewability, making it widely used in
various industrial and civil fields.
Chemical Composition:
Stainless steel is an austenitic stainless steel that has a
composition of chromium, nickel, and manganese. Its chemical
composition is as follows:
| Grade | Chemical Composition (%) |
| c | si | Mn | P | s | Ni | Cr | Mo |
| 201 | ≤0.15 | ≤0.75 | 5.5-7.5 | ≤0.06 | ≤ 0.03 | 3.5-5.5 | 16.0-18.0 | - |
| 301 | ≤0.15 | ≤1.0 | ≤2.0 | ≤0.045 | ≤ 0.03 | 6.0-8.0 | 16.0-18.0 | - |
| 304 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤ 0.03 | 8.0-10.5 | 18.0-20.0 | - |
| 304L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.035 | ≤ 0.03 | 9.0-13.0 | 18.0-20.0 | - |
| 316 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤ 0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 |
| 316Ti | ≤0.08 | ≤0.75 | ≤2.0 | ≤0.045 | ≤0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 |
| 310S | ≤0.08 | ≤1.5 | ≤2.0 | ≤0.045 | ≤0.03 | 19-22 | 24-26 | |
| 316L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.045 | ≤ 0.03 | 12.0-15.0 | 16 .0-1 8.0 | 2.0-3.0 |
| 321 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.035 | ≤ 0.03 | 9.013 | 17.0-1 9.0 | - |
| 405 | ≤0.08 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.03 | 0.6 | 11.5-14.5 | |
| 409 | ≤0.08 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.03 | 0.6 | 11.5-14.5 | |
| 409L | ≤0.08 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.03 | 0.6 | 11.5-14.5 | |
| 410 | ≤0.15 | ≤1.0 | ≤1.0 | ≤0.035 | ≤ 0.03 | - | 11.5-13.5 | - |
| 430 | ≤0.12 | ≤0.75 | ≤1.0 | ≤0.040 | ≤ 0.03 | ≤0.60 | 16.0-18.0 | - |
| 420 | ≤0.05 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.03 | 0.75 | 12-14 | 0.5 |
| 430 | ≤0.12 | ≤1.0 | ≤1.0 | ≤0.04 | 0.03 | 0.5 | 16-18 | 0.75 |
| 444 | ≤0.025 | ≤1.0 | ≤1.0 | ≤0.04 | 0.03 | 1 | 17.5-19.5 | 1.75-2.5 |
| 904L | ≤0.02 | ≤1.0 | ≤2.0 | ≤0.045 | 0.035 | 23-28 | 19-23 | 4.0-5.0 |
| 2205 | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.03 | 0.02 | 4.5-6.5 | 22.0-23.0 | 3.0-3.5 |
| 2507 | ≤0.03 | ≤0.8 | ≤1.0 | ≤0.035 | 0.02 | 6.0-8.0 | 24-26 |
3.0-5.0 |
Product Name | Hot Sale Brushed 430 Stainless Steel Sheet for Household
Appliances, Home Appliance Parts |
Thickness | 0.3mm-16mm |
Width | 1000mm-2000mm |
Length | 2000 mm , 2438 mm , 3000 mm , 6000 mm OR as reqirement |
Finish | No.1 , 2B , HL , NO.4 , BA , SB ,1D , 2D , 2C , 2E , NO.5 , NO.9 |
Technical | Hot rolling,Cold rolling |
Standard | ASTM 240 , A480 , JIS G 4304 , EN 10088-2 |
Certification | MTC Type 3.1 , PMI , CO |
Delivery Time | 7 days if have stock |
Thickness and Width:
The thickness and width of stainless steel an vary according to
specific needs and applications. Generally speaking, the thickness
of stainless steel can range from a very thin few millimeters to
tens of millimeters, and the width is usually between tens of
millimeters and several meters.
| Grade | GB | ASTM | DIN | JIS | BS |
| 200 series stainless steel | 12Cr17Mn6Ni5N | 201 | 1.4371 | SUS201 | - |
| 12Cr18Mn8Ni5N | 201 | 1.4373 | SUS202 | 284S16 |
| 300 series stainless steel | 12Cr17Ni7 | 301 | 1.4319 | SUS301 | 301S21 |
| 06Cr19Ni10 | 304 | 1.4301 | SUS304 | 304S15 |
| 022Cr19Ni10 | 304L | 1.4306 | SUS304L | 304S12 |
| 06Cr19Ni10N | 304N | 1.4315 | SUS404N1 | - |
| 16Cr23Ni13 | 309 | 1.4828 | SUH309 | |
| 06Cr23Ni13 | 309S | 1.4833 | SUS309S | |
| 20Cr25Ni20 | 310 | 1.4821 | | |
| 06Cr25Ni20 | 310S | 1.4845 | SUS310S | |
| 06Cr17Ni12Mo2 | 316 | 1.4401 | SUS316 | 316S16 |
| 07Cr17Ni12Mo2 | 316H | 1.4436 | | |
| 06Cr17Ni12Mo3Ti | 316Ti | 1.4571 | SUS316Ti | 320S31 |
| 022Cr17Ni12Mo2 | 316L | 1.4404 | SUS316L | 316S12 |
| 022Cr17Ni13Mo2N | 316LN | 1.4429 | SUS316LN | 316S61 |
| 06Cr19Ni13Mo3 | 317 | 1.4436 | SUS317 | 317S16 |
| 022Cr19Ni13Mo3 | 317L | 1.4438 | SUS317L | 317S12 |
| 06Cr18Ni9Ti | 321 | 1.4541 | SUS321 | 321S12 |
| 06Cr18Ni11Nb | 347 | 1.4550 | SUS347 | 347S17 |
| 07Cr18Ni11Nb | 347H | 1.4912 | SUS347H | |
| Duplex stainless steel | 015Cr20Ni18Mo6CuN | 254SMo | 1.4547 | | |
| 015Cr21Ni26Mo5Cu2 | 904L | 1.4539 | | |
| 06Cr26Ni4Mo2 | 329 | | SUS329J1 | |
| 022Cr19Ni5Mo3Si2N | 3RE60 | 1.4417 | DP11 | |
| 022Cr22Ni5Mo3N | F51 | 1.4462 | SUS329J3L/DP8 | |
| 022Cr23Ni5Mo3N | F60 | | | |
| 022Cr25Ni7Mo4N | F53 | 1.4410 | | |
| 03Cr25Ni6Mo3Cu2N | F61 | 1.4507 | SUS329J4L | |
| 022Cr25Ni7Mo4CuWN | F55 | 1.4362 | DP11 | |
| 022Cr23Ni4MoCuN | | 1.4362 | DP11 | |
| 022Cr25Ni6Mo2N | | 1.4460 | | |
| Precipitation hardening type stainless steel | 05Cr15Ni5Cu4Nb | 15-5PH | 1.4545 | XM-12 | |
| 05Cr17Ni4Cu4Nb | 17-4PH | 1.4542 | | |
| 07Cr17Ni7Al | 17-7PH | 1.4568 | | |
| 400 series stainless steel | 06Cr13Al | 405 | 1.4002 | SUS405 | 405S17 |
| 06Cr111Ti | 409 | | SUS409 | |
| 022Cr111Ti | 409L | 1.4512 | SUH409L | |
| 10Cr17 | 430 | 1.4016 | SUS430 | 430S15 |
| Y10Cr17 | 430F | 1.4104 | SUS430F | |
| 019Cr19Mo2NbTi | 444 | 1.4521 | SUS444 | |
| 06Cr13 | 410S | 1.4000 | SUS410S | 430S17 |
| 12Cr13 | 410 | 1.406 | SUS410 | 410S21 |
| 2Cr13 | 420 | 1.4021 | SUS420J1 | 420S37 |
| 3Cr13 | 420 | 1.4028 | SUS420J2 | 420S45 |
| 17Cr16Ni2 | 431 | 1.4057 | SUS431 | 431S29 |
| 108Cr17 | 440C | 1.4125 | SUS440S | |
| Y108Cr17 | 440F | | SUS440F | |
We can provide different specifications and sizes of stainless
steel, and can choose the appropriate thickness and width according
to the specific needs.
Hot Rolled and Cold Rolled
Stainless steel products can be manufactured using either hot
rolled or cold rolled techniques. Hot rolling involves heating the
steel above its recrystallization temperature and then passing it
through rollers to form the desired shape. Cold rolling, on the
other hand, involves passing the steel through rollers at room
temperature to reduce its thickness.
Different Finishes
Stainless steel comes in different finishes that can affect its
appearance and properties. Here are some common finishes:
| Different Finishes |
| 2B: This is a smooth, reflective finish that is produced by cold
rolling followed by annealing and descaling. |
| No.1: This is a rough, dull finish that is produced by hot rolling
followed by annealing and pickling. |
| SB: This is a satin finish that is produced by applying a fine
abrasive material to the surface of the steel. |
| BA: This is a bright, mirror-like finish that is produced by
buffing the surface of the steel with a fine abrasive material. |
| HL: This is a hairline finish that is produced by brushing the
surface of the steel with a fine abrasive material. |
| Mirror: This is a highly reflective finish that is produced by
polishing the surface of the steel with a very fine abrasive
material. |